Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting

Dongguan Ampfort Electronics Co., Ltd.
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now
    Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers
     
    Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers
    • Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers
    • Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers
    • Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers
    • Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers
    • Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers
    • Buy cheap Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting from wholesalers

    Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting

    Ask Lasest Price
    Brand Name : AMPFORT
    Model Number : MZ21-08D112M-102
    Certification : ROHS
    Price : 0.3 USD/PC
    Payment Terms : T/T, Western Union
    Supply Ability : 100KKPCS Per month
    Delivery Time : 3-4 weeks
    • Product Details
    • Company Profile

    Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting


    Ceramic PTC Thermistor YS4020 Cross Resettable Fuse 1000V 1100 Ohm 20% Tol For Current Limiting


    DESCRIPTION Of The Ceramic PTC Thermistor


    PTC THERMISTOR INTENDED FOR USE AS A CURRENT LIMITING PROTECTION DEVICE


    Outline size Of The Ceramic PTC Thermistor


    Model NumberMZ21-08D112M-102
    Dmax(mm)9.0
    Tmax(mm)6.5
    W (mm)5±1
    d(mm)0.6±0.05
    L1min(mm)10
    Hmax (mm)13.5
    Part NumberMZ21-08D112M-102
    Product MarkingSCD
    102R
    Coating Material and ColorGreen,Silicone Resin
    LeadTin – plated copper wire / Short lead / Side-bend

    Electrical Characteristics (Ta =25℃) Of The Ceramic PTC Thermistor


    Part NumberMZ21-08D112M-102
    Rated Resistance Rn (Ω)1100±20%
    Switching Temp. Tc(℃)80±10
    Withstand voltage Up(V)≥1000
    Rated Current In(mA)10(25±2℃)
    Switching Current It(mA)30(25±2℃)
    Residual Current Ir(mA)≤2
    Voltage Surge V(V)1000

    Test item and conditions Of The Ceramic PTC Thermistor


    NOTest ItemTest ConditionRequirements
    1

    Appearance

    Overall Dimension

    Rated zero power resistance

    No visual damage,Pin no oxidation, no broken;Mark shall be complete, clear and identifiable.

    Measure by vernier caliper.

    Room Temperature:25±2℃;Place period:≥30min

    Fig.1


    Table 1

    Table 2

    2Switching TempertureCurie temperature is corresponding value at 2 times of R25 R-T curve.Table 2
    3Withstand voltageAt 25±2℃ ambient environment,voltage 220V,last for 3S ;suddenly changed to 1000V, last 30S then cut off power .

    1000

    Visual appearance no visible damage

    4Non-Operating CurrentPlace in 25±2℃ still air for 30min, power voltage:220VAC,applying with 30mA current,last 1h ,test its resistance change ratio(Test voltage between two PTC lead with voltmeter ,test PTC current with amperemeter ,then can get resistance of PTC).

    10mA(25±2℃)

    ┃ Resistance change rate ┃≤50%

    Inaction for 1 hour

    5

    Action Current


    After placed in 25±2℃ still air for 30min , power voltage:220VAC,applying with 60Ma current, should go into high-impedance-state in 5 mins.

    30mA

    Action time ≤5min

    6Residual currentAt 25±2℃ ambient environment,adjust voltage withstand tester to 1000V gradually , steady 10s get reading -current go through PTC,it is residual curent.≤2mA
    7SolderabilityUse method of slotted weld ,stain with scaling powder , dip into 230±5℃ lead free tin(Sn96.5Ag3Cu0.5)molten solder groove along the axis direction, last for 3S~5S,body is 5mm far away with molten solder , take out and observe.The terminals shall be uniformly tinned, and its area≥95%
    8Resistance to soldering HeatUse method of slotted weld ,stain with scaling powder , dip into 260±5℃ lead free tin(Sn96.5Ag3Cu0.5)molten solder groove along the axis direction ,last for 3±1S,body is 2mm far away with molten solder,after place in room temperature for 24hours,check appearance and test zero power resistance then compare with initial resistance.

    No visible mechanical damage.

    ┃Resistance change rate┃≤ 20%

    9High temperature discontinuous loadAccording to GB7153 1081th experiment,temp 60±2℃,voltage 265V,initial current 400mA,power on 90min,outage 30min,after total load 1000 hours , place in room temperature for 24hours,check appearance and test zero power resistance then compare with initial resistance.

    No visible mechanical damage.

    ┃Resistance change rate┃≤ 30%

    10Strength of lead terminalDo experiment according to GB2423-29 test U , test Ua, tension 10N and keep 10s ; test Ub , bend 90°,tension 5N,consecutive 2 times ;test Uc , turn around 180° ,consecutive 2 times ; Place in room temperature for 24 hours,test zero power resistance and compare with initial resistance.┃Resistance change rate┃≤ 20%

    Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting

    Quality Ceramic PTC Thermistor YS4020 Cross Resettable 1000V 1100 Ohm 20% Tol For Current Limiting for sale
    Inquiry Cart 0
    Send your message to this supplier
     
    *From:
    *To: Dongguan Ampfort Electronics Co., Ltd.
    *Subject:
    *Message:
    Characters Remaining: (0/3000)